摘要
Using rare earth and zinc coordination polymers with aromatic carboxylic acids as the precursors, composing with the polyethylene glycol (PEG) as the dispersing media, micro crystalline phosphors Zn_3(PO_4)_2∶Eu 3+ and LaPO_4∶Eu 3+ were synthesized by in-situ co-precipitation method. X-ray diffraction and scanning electronic micrograph were used to characterize the resultant samples, whose particle size are in the range of micrometer. The emission spectra of Zn_3(PO_4)_2∶Eu 3+ (λ_ ex=245 nm) and LaPO_4∶Eu 3+ (λ_ ex=390 nm) shows that the emission for Eu 3+ in Zn_3(PO_4)_2 is dominated by the 5D_0→7F_1 (592 nm) magnetic-dipole transition,While the dominant emission for Eu 3+ in LaPO_4 is the typical hypersensitive transition 5D_0→7F_2 (618 nm).
Using rare earth and zinc coordination polymers with aromatic carboxylic acids as the precursors, composing with the polyethylene glycol (PEG) as the dispersing media, micro crystalline phosphors Zn_3(PO_4)_2∶Eu 3+ and LaPO_4∶Eu 3+ were synthesized by in-situ co-precipitation method. X-ray diffraction and scanning electronic micrograph were used to characterize the resultant samples, whose particle size are in the range of micrometer. The emission spectra of Zn_3(PO_4)_2∶Eu 3+ (λ_ ex=245 nm) and LaPO_4∶Eu 3+ (λ_ ex=390 nm) shows that the emission for Eu 3+ in Zn_3(PO_4)_2 is dominated by the 5D_0→7F_1 (592 nm) magnetic-dipole transition,While the dominant emission for Eu 3+ in LaPO_4 is the typical hypersensitive transition 5D_0→7F_2 (618 nm).
基金
ProjectsupportedbytheScienceFundofShanghaiUniversitiesforExcellentYouthScientists