The sample La_ 0.3Ca_ 0.7Mn_ 0.96W_ 0.04O_3 was prepared by the solid-state method. Magnetic properties of La_ 0.3Ca_ 0.7Mn_ 0.96W_ 0.04O_3 was studied through the measurement of M-T curve, M-H curves and ESR curves of the sample. The results show that: charge ordering (CO) phase forms at 265 K; the system exhibits paramagnetism when T>265 K; it exhibits long-range anti-ferromagnetism (there is a little FM component in AFM background) and the coexistence of a little FM phase and AFM/CO phase forms when T<225 K; the system transforms from paramagnetism to antiferromagnetism in charge-ordering state with temperature decreasing from 265 to 225 K. The width of ESR spectrum line of the sample La_ 0.3Ca_ 0.7Mn_ 0.96W_ 0.04O_3 was measured, and the value of the line width of paramagnetic resonance ΔH_ PP increases with temperature decreasing, which indicates that ferromagnetic connection of the sample strengthens with temperature decreasing.
The sample La_ 0.3Ca_ 0.7Mn_ 0.96W_ 0.04O_3 was prepared by the solid-state method. Magnetic properties of La_ 0.3Ca_ 0.7Mn_ 0.96W_ 0.04O_3 was studied through the measurement of M-T curve, M-H curves and ESR curves of the sample. The results show that: charge ordering (CO) phase forms at 265 K; the system exhibits paramagnetism when T>265 K; it exhibits long-range anti-ferromagnetism (there is a little FM component in AFM background) and the coexistence of a little FM phase and AFM/CO phase forms when T<225 K; the system transforms from paramagnetism to antiferromagnetism in charge-ordering state with temperature decreasing from 265 to 225 K. The width of ESR spectrum line of the sample La_ 0.3Ca_ 0.7Mn_ 0.96W_ 0.04O_3 was measured, and the value of the line width of paramagnetic resonance ΔH_ PP increases with temperature decreasing, which indicates that ferromagnetic connection of the sample strengthens with temperature decreasing.
基金
ProjectsupportedbytheNationalNaturalScienceFoundationKeyProject(19934003)
NationalKeyFundamentalResearchProject(001CB610604)
NaturalScienceResearchProjectoftheEducationDepartmentofAnhuiProvince(2004KJ331)
NaturalScienceResearchProjectofCollegesandUniversitiesofAnhuiProvince(2005KJ234)