摘要
Pb_ 1-xLa_xTi_ 1-x/4O_3 nanocrystals with different amounts of lanthanum were prepared by modified sol-gel method and detected by FT-Raman spectra at 288 and 378 K, respectively. The improved synthetic technique used in this paper could obtain nanocrystals with apparently promoted synthetic speed from a few days to several hours (4 times faster of hydrolytic process than that of traditional sol-gel method and reduced preparation period of gel from 24 h to several hours) at relatively lower temperature by hydrolysis of sol to gel through adding methyl alcohol/water solution into sol under vigorous stirring and annealed the fresh gel directly. The effects of lanthanum′s amount, annealed temperature and nanocrystals′ grain size of Pb_ 0.9La_ 0.1Ti_ 0.975O_3 nanocrystals on frequency, shape and width of the phonon peak were also discussed in detail.
Pb_ 1-xLa_xTi_ 1-x/4O_3 nanocrystals with different amounts of lanthanum were prepared by modified sol-gel method and detected by FT-Raman spectra at 288 and 378 K, respectively. The improved synthetic technique used in this paper could obtain nanocrystals with apparently promoted synthetic speed from a few days to several hours (4 times faster of hydrolytic process than that of traditional sol-gel method and reduced preparation period of gel from 24 h to several hours) at relatively lower temperature by hydrolysis of sol to gel through adding methyl alcohol/water solution into sol under vigorous stirring and annealed the fresh gel directly. The effects of lanthanum′s amount, annealed temperature and nanocrystals′ grain size of Pb_ 0.9La_ 0.1Ti_ 0.975O_3 nanocrystals on frequency, shape and width of the phonon peak were also discussed in detail.
基金
ProjectsupportedbytheNationalNaturalScienceFoundationofChina(20171015)