Metallurgical coatings of iron-based alloy with RE oxide were prepared on low-carbon steel using a home-made DC-plasma jet surface metallurgy equipment. Scanning electron microscope (SEM), energy dispersive X-ray (EDX) microanalysis and X-ray diffraction analysis (XRD) were employed to observe the microstructure and analyze the chemical compositions of coatings. And the cracking susceptibility of coatings was studied in terms of RE addition. Experimental results show that addition of RE oxide (La_2O_3 and CeO_2) can refine and purify the microstructure, and can reduce the cracking susceptibility of coatings.
Metallurgical coatings of iron-based alloy with RE oxide were prepared on low-carbon steel using a home-made DC-plasma jet surface metallurgy equipment. Scanning electron microscope (SEM), energy dispersive X-ray (EDX) microanalysis and X-ray diffraction analysis (XRD) were employed to observe the microstructure and analyze the chemical compositions of coatings. And the cracking susceptibility of coatings was studied in terms of RE addition. Experimental results show that addition of RE oxide (La_2O_3 and CeO_2) can refine and purify the microstructure, and can reduce the cracking susceptibility of coatings.
基金
ProjectsupportedbytheNaturalScienceFoundationofShandongProvince(Y2002F12)