摘要
K3C60 single crystal film was prepared on the cleaved (111) surface of C60 single crystal. Synchrotron radiation angle-resolved photoemission spectra were measured at normal emission with sample temperature at - 150K. Up to four subpeaks of LUMO-derived band were observed. These sub-peaks exhibit distinct energy dispersions which resemble in general the theoretical ones calculated for K3C60 at low temperature with the so-called one-dimensional disordered structure. But there is large deviation of experimental sub-band intervals from the theoretical values. This result is meaningful for the studies of the physical properties of alkali-doped C60 solids, e.g. the mechanism for superconductivity.
K_3C_(60) single crystal film was prepared on the cleaved (111) surface of C60 single crystal. Synchrotron radiation angle-resolved photoemission spectra were measured at normal emission with sample temperature at - 150K. Up to four subpeaks of LUMO-derived band were observed. These sub-peaks exhibit distinct energy dispersions which resemble in general the theoretical ones calculated for K3C60 at low temperature with the so-called one-dimensional disordered structure. But there is large deviation of experimental sub-band intervals from the theoretical values. This result is meaningful for the studies of the physical properties of alkali-doped C60 solids, e.g. the mechanism for superconductivity.