Base on a vast amount of testing and calculations for the welding thermal cycling curves of different testing points in fusion welding (TIG welding, gas welding) HAZ of zinc-based alloy with low melting points, this paper defines the welding thermal cycle parameters of microstructure stimulation of HAZ by zinc-based alloy fusion welding process. On the principle of which the microstrnct,are and harkness of the testing points in simulation specimens are basically correspondence with that of actual welding HAZ, the microstructure simulation of testing points Tm=370O℃. 305℃) of ZA12 alloy by fusion welding is carried out by the means of omhic-heating welding thermal simulation tester. The study results of the abrasion-resistance of simulation specimens HAZ by fusion welding process indicates that the abmsion-resistance is closely related to the form of eutectoid microstructure in or in the structure.
Base on a vast amount of testing and calculations for the welding thermal cycling curves of different testing points in fusion welding (TIG welding, gas welding) HAZ of zinc-based alloy with low melting points, this paper defines the welding thermal cycle parameters of microstructure stimulation of HAZ by zinc-based alloy fusion welding process. On the principle of which the microstrnct,are and harkness of the testing points in simulation specimens are basically correspondence with that of actual welding HAZ, the microstructure simulation of testing points Tm=370O℃. 305℃) of ZA12 alloy by fusion welding is carried out by the means of omhic-heating welding thermal simulation tester. The study results of the abrasion-resistance of simulation specimens HAZ by fusion welding process indicates that the abmsion-resistance is closely related to the form of eutectoid microstructure in or in the structure.