Mono(isopropyl maleate-oyloxyl) diisopropoxyl dysprosium(DM) was synthesized by the reaction of dysprosium isopropoxide with maleic anhydride. Dy-containing polymer(PDM) was obtained by the solution polymerization of DM using 2, 2'-azobisisobutyronitrile (AIBN) as an initiator. The kinetic study on the polymerization shows that the polymerization of DM exhibits high apparent activation energy(96.3 kJ.mol(-1)), indicating that the activity of DM is low for polymerization. The kinetic equation of polymerization can be expressed as R-P = k(P)C(DM)(1.23)c(AIBN)(0.82). The polymeric solid material shows excellent heat-stability and strong characteristic fluorescence of Dy3+, (4)Fg(9/2) --> H-6(15/2) and F-4(9/2) --> H-6(13/2).
Mono(isopropyl maleate-oyloxyl) diisopropoxyl dysprosium(DM) was synthesized by the reaction of dysprosium isopropoxide with maleic anhydride. Dy-containing polymer(PDM) was obtained by the solution polymerization of DM using 2, 2'-azobisisobutyronitrile (AIBN) as an initiator. The kinetic study on the polymerization shows that the polymerization of DM exhibits high apparent activation energy(96.3 kJ.mol(-1)), indicating that the activity of DM is low for polymerization. The kinetic equation of polymerization can be expressed as R-P = k(P)C(DM)(1.23)c(AIBN)(0.82). The polymeric solid material shows excellent heat-stability and strong characteristic fluorescence of Dy3+, (4)Fg(9/2) --> H-6(15/2) and F-4(9/2) --> H-6(13/2).
基金
ProjectsupportedbyFujianProvincialNaturalScienceFoundationofChina(B970 11)