The rare earth complex Eu(TTA) 3 was successfully encapsulated into MCM 41 mesoporous molecular sieve by the addition of the complex into the sol gel mixture for the synthesis of MCM 41 mesoporous material under microwave radiation. The as synthesized MCM 41 hosted Eu(TTA) 3 mesophase was confirmed to possess hexagonally ordered mesostructure and a uniform crystal size of about 30 nm with XRD and HRTEM techniques. Moreover, the IR spectrum, photoluminescence effect and fluorescence lifetime of the Eu(TTA) 3/MCM 41 hybrid were also studied. An increase in Stokes' shift and no change in luminescence lifetime were observed to the resultant mesophase in comparison with Eu(TTA) 3 in ethanol solution.
The rare earth complex Eu(TTA) 3 was successfully encapsulated into MCM 41 mesoporous molecular sieve by the addition of the complex into the sol gel mixture for the synthesis of MCM 41 mesoporous material under microwave radiation. The as synthesized MCM 41 hosted Eu(TTA) 3 mesophase was confirmed to possess hexagonally ordered mesostructure and a uniform crystal size of about 30 nm with XRD and HRTEM techniques. Moreover, the IR spectrum, photoluminescence effect and fluorescence lifetime of the Eu(TTA) 3/MCM 41 hybrid were also studied. An increase in Stokes' shift and no change in luminescence lifetime were observed to the resultant mesophase in comparison with Eu(TTA) 3 in ethanol solution.
基金
ProjectsupportedbytheScienceFoundationofZhongshanUniversity (32 0 0 90 1 )andLaboratoryofRareEarthChemistryandPhysics
Changc