Three kinds of lithium cobalt oxides with lithium to cobalt atomic ratios of 0.6, 0.8 and 1.0 respectively were prepared using nitrates and citric acid by sol gel process. During the baking of the dry gel powder, two exothermic peaks occur, followed by the formation of Li 2O and Co 3O 4 and then the combination of LiCoO 2, which is testified by DTA and XRD. The powder formed from an alkaline sol is finer than that from the acidic one. There are a single phase intercalation of lithium ion and an electrochemical reduction reaction for higher valence cobalt ion when simulating the discharging process of Li B/LiCl KCl/lithium cobalt oxides at 500 ℃, and the voltage and specific capacity are not sensitive to the initial ratios of lithium to cobalt.
Three kinds of lithium cobalt oxides with lithium to cobalt atomic ratios of 0.6, 0.8 and 1.0 respectively were prepared using nitrates and citric acid by sol gel process. During the baking of the dry gel powder, two exothermic peaks occur, followed by the formation of Li 2O and Co 3O 4 and then the combination of LiCoO 2, which is testified by DTA and XRD. The powder formed from an alkaline sol is finer than that from the acidic one. There are a single phase intercalation of lithium ion and an electrochemical reduction reaction for higher valence cobalt ion when simulating the discharging process of Li B/LiCl KCl/lithium cobalt oxides at 500 ℃, and the voltage and specific capacity are not sensitive to the initial ratios of lithium to cobalt.
基金
The Doctoral Foundation of the Education Ministryof China!(No .960 5 3 3 11)