摘要
Alumina aerogels with high porosity of nanometer size were prepared from Al, n-butanol and ethyl acetoacetate by the sol-gel route and the N2 supercritical extraction drying technique. Optical experiment results showed that for alumina aerogels after annealing at 500℃ for 4 h one intense blue emission band appeared in the wavelength range of 400 to 800 nm, and the optical absorption edge moved from 8.0 eV of coarse grain Al203 to 3~eV and with increasing the annealing temperature, this luminescence band presented blue shifts. The reasons of these new optical properties are discussed in detail.
Alumina aerogels with high porosity of nanometer size were prepared from Al, n-butanol and ethyl acetoacetate by the sol-gel route and the N2 supercritical extraction drying technique. Optical experiment results showed that for alumina aerogels after annealing at 500℃ for 4 h one intense blue emission band appeared in the wavelength range of 400 to 800 nm, and the optical absorption edge moved from 8.0 eV of coarse grain Al203 to 3~eV and with increasing the annealing temperature, this luminescence band presented blue shifts. The reasons of these new optical properties are discussed in detail.