摘要
The magnetic aftereffect (MAE) and the positron lifetime were measured at room temperature on the Fe_73.5Cu_1 Nb_3Si_13.5 B_9 alloy in as-cast and after annealing at temperature T_a in the range from 450 to 750℃ It was found that both the MAE and the positron lifetime decrease with increasing T_a when T_≤600℃. While Ta≥650℃, MAE is essentially suppressed, and two positron lifetimes appear.
The magnetic aftereffect (MAE) and the positron lifetime were measured at room temperature on the Fe_73.5Cu_1 Nb_3Si_13.5 B_9 alloy in as-cast and after annealing at temperature T_a in the range from 450 to 750℃ It was found that both the MAE and the positron lifetime decrease with increasing T_a when T_≤600℃. While Ta≥650℃, MAE is essentially suppressed, and two positron lifetimes appear.