The threshold stress, σc, for sulfide stress corrosion cracking (SCC) of seven pipeline steels and five other steels, the critical stress, Sc, for seven pipeline steels and two drill rod steels with various strengths and the susceptibility to SCC, IRA or σf(SCC)/σf, for four pipeline steels, two drill rod steels and five other steels were measured. The results showed that there are no definite relationships among σc, Sc and IRA or σf(SCC)/σf.The threshold stress for hydrogen induced cracking (HlC) during charging with loading in the H2S04 solution, σc(H), decreased linearly with logarithm of the concentration of diffusible hydrogen c0, i.e., σc(H)=A-B Inco for four pipeline steels. σc(H) obtained with a special cathodic current ic, which was corresponding to the diffusible hydrogen concentration during immersing in the H2S solution, were consistent with /c for sulfide SCC for four pipeline steels. Therefore, σc for sulfide SCC can be measured using dynamically charging in the H2SO4 solution with the special cathodic current ic.
The threshold stress, σc, for sulfide stress corrosion cracking (SCC) of seven pipeline steels and five other steels, the critical stress, Sc, for seven pipeline steels and two drill rod steels with various strengths and the susceptibility to SCC, IRA or σf(SCC)/σf, for four pipeline steels, two drill rod steels and five other steels were measured. The results showed that there are no definite relationships among σc, Sc and IRA or σf(SCC)/σf.The threshold stress for hydrogen induced cracking (HlC) during charging with loading in the H2S04 solution, σc(H), decreased linearly with logarithm of the concentration of diffusible hydrogen c0, i.e., σc(H)=A-B Inco for four pipeline steels. σc(H) obtained with a special cathodic current ic, which was corresponding to the diffusible hydrogen concentration during immersing in the H2S solution, were consistent with /c for sulfide SCC for four pipeline steels. Therefore, σc for sulfide SCC can be measured using dynamically charging in the H2SO4 solution with the special cathodic current ic.
基金
This project was supported by the NNSFC of China! (No.19891180, 59725104, 59895150)
the Corporation of iron and Steel Baosha