摘要
Several concepts of the grain refinement mechanism of B on hypoeutectic Al-Si alloys have been adopted: the refining effect of B on the a-AI and eutectic Si with the different additions of Al-B master alloys made at 850℃ was investigated; and the Al-B master alloys formed under different temperature conditions have been studied to explore the morphologies of AIB2 particles; slowly cooled sample with addition of Al-B was made to explore the refinement mechanism. AI-B master alloy can refine not only a-AI, but eutectic Si. Theoretical analysis indicates that, although AIB2 does not take part directly in the nucleation process in pure Al in the presence of Si, it provides a substrate for precipitation of a small content of Si from which a-At will grow without any undercooling. When the temperature decreases to eutectic line, AIB2 subsequently nucleates eutectic Si; AIB2 particles appear in two different morphologies, namely, hexagonal platelet and tetradehedron morphology which depend on the processing temperature conditions.
Several concepts of the grain refinement mechanism of B on hypoeutectic Al-Si alloys have been adopted: the refining effect of B on the a-AI and eutectic Si with the different additions of Al-B master alloys made at 850℃ was investigated; and the Al-B master alloys formed under different temperature conditions have been studied to explore the morphologies of AIB2 particles; slowly cooled sample with addition of Al-B was made to explore the refinement mechanism. AI-B master alloy can refine not only a-AI, but eutectic Si. Theoretical analysis indicates that, although AIB2 does not take part directly in the nucleation process in pure Al in the presence of Si, it provides a substrate for precipitation of a small content of Si from which a-At will grow without any undercooling. When the temperature decreases to eutectic line, AIB2 subsequently nucleates eutectic Si; AIB2 particles appear in two different morphologies, namely, hexagonal platelet and tetradehedron morphology which depend on the processing temperature conditions.
基金
Shandong Natural Foundation !(Grant No:Z99F01)
the Natiotal Natals Science Foundation of China !(Grant NO.59671046).