The microstructure and the stability of Fe_73.5Cu_1Nb_3Si_13.5B_9 alloy at different stages of phase transformation were investigated through the observation of X-ray difraction and transmission electron microscopy and the measurement of magnetic aftereffect (MAE). It was found that the dependence of the volume fraction of amorphous phase and the MAE in the samples annealed from 450 to 700℃ on the annealing temperature is similar.
The microstructure and the stability of Fe_73.5Cu_1Nb_3Si_13.5B_9 alloy at different stages of phase transformation were investigated through the observation of X-ray difraction and transmission electron microscopy and the measurement of magnetic aftereffect (MAE). It was found that the dependence of the volume fraction of amorphous phase and the MAE in the samples annealed from 450 to 700℃ on the annealing temperature is similar.