摘要
Preparing method and processing of Tb-Dy-Fe alloy samples with [110] axial orientation as well as their magnetostrictive properties have been studied. It has been found that the magnetostrictive strains of polycrystal samples with [110] axial orientation can reach (1550-1900) ×10~-6 in a low magnetic field less than 80 kA/m, which are equal to or somewhat better than that of the polycrystal samples with [112] axial orientation.
Preparing method and processing of Tb-Dy-Fe alloy samples with [110] axial orientation as well as their magnetostrictive properties have been studied. It has been found that the magnetostrictive strains of polycrystal samples with [110] axial orientation can reach (1550-1900) ×10^-6 in a low magnetic field less than 80 kA/m, which are equal to or somewhat better than that of the polycrystal samples with [112] axial orientation.