By continuous quenching process, the effect of austenitizing temperature and time on the structure and hardness of bainiteductile cast iron was studied. It was found that (l) low austenitizing temperature would result in scrap ferrite existing in matrix, whichreduces the macro-hardness of bainite ductile cast iron; (2) high austenitizing temperature would make carbide decomposed, which alsoinduces the macro-hardness of bainite cast iron, and (3) austenitizing time has little effect on the structure of bainite ductile cast iron, butas it increases, the macro-hardness ofbainite ductile cast iron and micro-hardness of bainite increases. To the ductile cast iron, as a result,the suitable austenitizing temperature and time are recommended as 880 and 120 min respectively.
By continuous quenching process, the effect of austenitizing temperature and time on the structure and hardness of bainiteductile cast iron was studied. It was found that (l) low austenitizing temperature would result in scrap ferrite existing in matrix, whichreduces the macro-hardness of bainite ductile cast iron; (2) high austenitizing temperature would make carbide decomposed, which alsoinduces the macro-hardness of bainite cast iron, and (3) austenitizing time has little effect on the structure of bainite ductile cast iron, butas it increases, the macro-hardness ofbainite ductile cast iron and micro-hardness of bainite increases. To the ductile cast iron, as a result,the suitable austenitizing temperature and time are recommended as 880 and 120 min respectively.