摘要
A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of eliminating them was proposed. The resultsshow that (l) the brittle Al,Ti particulates are always present in the composites when the molar ratio of Ti to B 'T,:nB is l:2; and (2) theformation of the brittle Al,Ti phase can be avoided entirely from the final product by using a proper 'T,:nB of l:4 in the Ti-B-Al preforms.In the former case, the tensile elongation of the composite is only 4%, much lower than the value of pure aluminum (20%). In the latercase, the tensile elongation of this composite is 10%, higher than the value of the composite with a lot ofAl,Ti (4%), whereas the ultimatetensile stfength of the former is nearly that of the later.
A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of eliminating them was proposed. The resultsshow that (l) the brittle Al,Ti particulates are always present in the composites when the molar ratio of Ti to B 'T,:nB is l:2; and (2) theformation of the brittle Al,Ti phase can be avoided entirely from the final product by using a proper 'T,:nB of l:4 in the Ti-B-Al preforms.In the former case, the tensile elongation of the composite is only 4%, much lower than the value of pure aluminum (20%). In the latercase, the tensile elongation of this composite is 10%, higher than the value of the composite with a lot ofAl,Ti (4%), whereas the ultimatetensile stfength of the former is nearly that of the later.