摘要
The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic with lattice parameters a =0.74569(3) nm, b =0.76851(5) nm, c =0.45676(8) nm, V =0.26176 nm 3, Z =4 and D x=8.076 g·cm -3 , space group Pna2 1(33). The figure of merit F N for the compound is F 30 =54 (0.0093, 60).
The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic with lattice parameters a =0.74569(3) nm, b =0.76851(5) nm, c =0.45676(8) nm, V =0.26176 nm 3, Z =4 and D x=8.076 g·cm -3 , space group Pna2 1(33). The figure of merit F N for the compound is F 30 =54 (0.0093, 60).