摘要
The crack morphologies of hardfacing metal were observed by means of optical microscope and scanning electron microscope. Meanwhile, the cracking resistances of hardfacing metal were investigated. The results show that the solidification cracking and quench hardened cracking are the main forms of cracking in hardfacing metal. The cracking resistance of hardfacing metal can be improved by adding rare earth oxide in the coat of electrode.
The crack morphologies of hardfacing metal were observed by means of optical microscope and scanning electron microscope. Meanwhile, the cracking resistances of hardfacing metal were investigated. The results show that the solidification cracking and quench hardened cracking are the main forms of cracking in hardfacing metal. The cracking resistance of hardfacing metal can be improved by adding rare earth oxide in the coat of electrode.