In this paper it is-discussed on the mechanism of upper bainite formation. According to the results obtained in Fe-1.36Si-1.01Cr-0.88C steel, we discovered that the primary upper bainite is formed by subunits arranging along its long axis and steps are formed by subunits growing into different size-along the thickness, the macro-plane of the primary upper bainite plate is the same as the basal plane (shear plane), the formation mechanism of the primary upper bainite plate is the nucleation-growth mechanism of subunits shearing one by one along long axis, controlled by diffusion.
In this paper it is-discussed on the mechanism of upper bainite formation. According to the results obtained in Fe-1.36Si-1.01Cr-0.88C steel, we discovered that the primary upper bainite is formed by subunits arranging along its long axis and steps are formed by subunits growing into different size-along the thickness, the macro-plane of the primary upper bainite plate is the same as the basal plane (shear plane), the formation mechanism of the primary upper bainite plate is the nucleation-growth mechanism of subunits shearing one by one along long axis, controlled by diffusion.