Based on the test results obtained from the single-step test and the incremental-step test at room temperature and 240℃, a probabilistic assessment of temperature effects on the cyclic stress-strum response and the fatigue life of 1Cr18Ni9Ti steel weld metal is performed. In orber to assess the temperature effect on cyclic stress amplitude where there is a scatter of the material cyclic constitution, a probabilistic assessment approach on the basis of probabilistic modified Ramberg-Osgood relations is introduced.The investigation shows that the cyclic stress amplitude and the scatter of cyclic stress amplitude data are decreased at 240℃. Similarly, from the consideration of the fatigue life scatter a probabilistic assessment of temperature effect on the fatigue life is suggested on the basis of probabilistic Langer S-N relations. The investigation shows that the crack initiation life is increased and the scatter of crack initiation life data is decreased at 240℃.
Based on the test results obtained from the single-step test and the incremental-step test at room temperature and 240℃, a probabilistic assessment of temperature effects on the cyclic stress-strum response and the fatigue life of 1Cr18Ni9Ti steel weld metal is performed. In orber to assess the temperature effect on cyclic stress amplitude where there is a scatter of the material cyclic constitution, a probabilistic assessment approach on the basis of probabilistic modified Ramberg-Osgood relations is introduced.The investigation shows that the cyclic stress amplitude and the scatter of cyclic stress amplitude data are decreased at 240℃. Similarly, from the consideration of the fatigue life scatter a probabilistic assessment of temperature effect on the fatigue life is suggested on the basis of probabilistic Langer S-N relations. The investigation shows that the crack initiation life is increased and the scatter of crack initiation life data is decreased at 240℃.