摘要
The liquidus of the ternary Ag-Cd-Si alloy system in the Ag-Cu rich region was determined by DTA. The ternary Ag-Cd-Si system was divided into two ternary systems Ag-Cu-Cuo.76Si0.24 and Ag-Cu0.76Si0.24-Si by the section of Ag-Cu0.76 Si0.24.There is one ternary eutectic point for both the systems with the composition of 12. 5at. %Ag+71. 7at.%Cu+15.8at. %Si and 30at.% Ag+44.7at.%Cu+25.3at.%Sirespectivelg and the temperatures of the eutectic points are 740 and 705℃ respectively.
The liquidus of the ternary Ag-Cd-Si alloy system in the Ag-Cu rich region was determined by DTA. The ternary Ag-Cd-Si system was divided into two ternary systems Ag-Cu-Cuo.76Si0.24 and Ag-Cu0.76Si0.24-Si by the section of Ag-Cu0.76 Si0.24.There is one ternary eutectic point for both the systems with the composition of 12. 5at. %Ag+71. 7at.%Cu+15.8at. %Si and 30at.% Ag+44.7at.%Cu+25.3at.%Sirespectivelg and the temperatures of the eutectic points are 740 and 705℃ respectively.