In this paper,the superplastic characteristics of the beta-SiC whisker reinforced 2024aluminum composite, fabricated by squeeze casting and hot-rolling after extrusion were investigated. The compsite had a fine grain size of about 2μm, and exhibited a strain rate sensitivity of about 0.35 and a maximum elongation of 350% at an initial strain rate of 1.1×10-1s-1 at 803K. In addition, the superplastic deformation mechanisme of the composite were also examined.
In this paper,the superplastic characteristics of the beta-SiC whisker reinforced 2024aluminum composite, fabricated by squeeze casting and hot-rolling after extrusion were investigated. The compsite had a fine grain size of about 2μm, and exhibited a strain rate sensitivity of about 0.35 and a maximum elongation of 350% at an initial strain rate of 1.1×10-1s-1 at 803K. In addition, the superplastic deformation mechanisme of the composite were also examined.