摘要
The texture of 80% cold rolling CuZn ordered alloy was investigated. The development of rolling texturein 50%Cu-50%Zn(at.) alloy has been characterized by a inhomogenous {111} fiber texture with strong {111} <112>component, which is significantly different from the conventional Cu-Zn alloys. The main characters of cold rollingtextures in ordered CuZn alloy are obviously similar to that in IF steel with bcc structure or ordered Fe3A1-basedalloys with imperfect B2 structure. From the rolling texture obtained by experiments and simulations,it can be estimated that main deformation mechanism are characterized by the activation of slip systems with <111> Burgersvector in CuZn ordered alloy.
The texture of 80% cold rolling CuZn ordered alloy was investigated. The development of rolling texturein 50%Cu-50%Zn(at.) alloy has been characterized by a inhomogenous {111} fiber texture with strong {111} <112>component, which is significantly different from the conventional Cu-Zn alloys. The main characters of cold rollingtextures in ordered CuZn alloy are obviously similar to that in IF steel with bcc structure or ordered Fe3A1-basedalloys with imperfect B2 structure. From the rolling texture obtained by experiments and simulations,it can be estimated that main deformation mechanism are characterized by the activation of slip systems with <111> Burgersvector in CuZn ordered alloy.