ACTIVATIONENERGYOFFeAlALLOYSDURINGSUPERPLASTICDEFORMATION①LiDingqiang,LinDongliang(T.L.Lin)ThePublicLaboratoryofHighTemperatu...
The activation energy of large grained FeAl alloys during superplastic deformation has been investigated. The flow activation energy was measured to be about 370, 290 and 260 kJ·mol -1 forFe 36.5Al, Fe 36.5Al 1Ti and Fe 36.5Al 2Ti(mole fraction, %) alloys, respectively, which are much lower than the creep activation energy previously measured in FeAl alloys. Ti addition can decrease the grain size and the activation energy of FeAl alloy.
出处
《中国有色金属学会会刊:英文版》
CSCD
1997年第4期17-20,共4页
Transactions of Nonferrous Metals Society of China