摘要
The electrical resistivity and viscosity of liquid hypoeutectic Al 7%Si and hypereutectic Al 18%Si alloys, and the influences of trace strontium and phosphorus on them were investigated. The trace additions of the two elements increase the electrical resistivity. At the precipitation temperatures of primary phase, the electrical resistivity exhibits a discontinuity for all experimental Al Si alloys. In the discontinuity the electrical resistivity, respectively, decreases and increases abruptly for Al 7%Si alloys and Al 18%Si alloys. Phosphorus and strontium both have some effects on the discontinuity temperature and the jump value of electrical resistivity of Al 18%Si alloys, but strontium hardly has effect on them in Al 7%Si alloys. The trace additions of strontium and phosphorus increase the viscosity of the experimental alloy.
The electrical resistivity and viscosity of liquid hypoeutectic Al 7%Si and hypereutectic Al 18%Si alloys, and the influences of trace strontium and phosphorus on them were investigated. The trace additions of the two elements increase the electrical resistivity. At the precipitation temperatures of primary phase, the electrical resistivity exhibits a discontinuity for all experimental Al Si alloys. In the discontinuity the electrical resistivity, respectively, decreases and increases abruptly for Al 7%Si alloys and Al 18%Si alloys. Phosphorus and strontium both have some effects on the discontinuity temperature and the jump value of electrical resistivity of Al 18%Si alloys, but strontium hardly has effect on them in Al 7%Si alloys. The trace additions of strontium and phosphorus increase the viscosity of the experimental alloy.
出处
《中国有色金属学会会刊:英文版》
CSCD
1997年第4期68-72,共5页
Transactions of Nonferrous Metals Society of China