摘要
The compound NdFe 0.6 Sb 2 was studied by means of X ray powder diffraction. The X ray powder diffraction data and structural parameters demonstrated that this compound is of the tetragonal structure with space group P4/nmm, Z =2 and D x=7.615 g·cm -3 . The lattice parameters are a =0.43499 (1) nm and c =0.97083 (4) nm. Refinement was performed with 42 reflections.
The compound NdFe 0.6 Sb 2 was studied by means of X ray powder diffraction. The X ray powder diffraction data and structural parameters demonstrated that this compound is of the tetragonal structure with space group P4/nmm, Z =2 and D x=7.615 g·cm -3 . The lattice parameters are a =0.43499 (1) nm and c =0.97083 (4) nm. Refinement was performed with 42 reflections.