Potential’s fluctuation of rust preventing oil film during its degradation was studied using wirebeam electrode. Being non-destructive and simple, potential measurement is a very repetitive method. Otherelectrochemical testing method, e. g., polarization resistance, can breakdown the integrity of oil coating byDC current; EIS is time consuming. As a special electrochemical sensor, wire beam electrode contains 101wires of mild steel wires, and it is helpful to improve the reproducibility of electrochemical test evidently.Using this electrode, the electrochemical parameters and their distribution which was related to under filmcorrosion process are measured directly so as to describe potential’s fluctuation of rust preventing oil film. Itis pointed out that there is potential’s fluctuation on rust preventing oil film during its degradation, and thischaracteristic has direct effect on the self-repairing ability of rust preventing oil film. However, for the uncoated metal electrode and base oil film, there is no such behavior. It is also pointed out that inhibitors in theoil film have direct effect on its self-repairing ability.
Potential's fluctuation of rust preventing oil film during its degradation was studied using wirebeam electrode. Being non-destructive and simple, potential measurement is a very repetitive method. Otherelectrochemical testing method, e. g., polarization resistance, can breakdown the integrity of oil coating byDC current; EIS is time consuming. As a special electrochemical sensor, wire beam electrode contains 101wires of mild steel wires, and it is helpful to improve the reproducibility of electrochemical test evidently.Using this electrode, the electrochemical parameters and their distribution which was related to under filmcorrosion process are measured directly so as to describe potential's fluctuation of rust preventing oil film. Itis pointed out that there is potential's fluctuation on rust preventing oil film during its degradation, and thischaracteristic has direct effect on the self-repairing ability of rust preventing oil film. However, for the uncoated metal electrode and base oil film, there is no such behavior. It is also pointed out that inhibitors in theoil film have direct effect on its self-repairing ability.