摘要
The magnetic properties, structure defects of electrodeposited Fe-Ni-P alloys with various compositions and the thermostability at amorphous state have been studied by DSC, positron annihilation and electronic integrating instrument methods. The results show that the thermostability of amorphous Fe-Ni-P alloys increases with Fe content. Emergence and recrystallization of stable phases defer as the P content of the coating increases. The minimum H-c, B-r and P-h occur at 9.4 P (wt pet) content. Maximum H-c, B-r and P-h occur at the weight ratio of Fe to Ni equaling to 1/9.
The magnetic properties, structure defects of electrodeposited Fe-Ni-P alloys with various compositions and the thermostability at amorphous state have been studied by DSC, positron annihilation and electronic integrating instrument methods. The results show that the thermostability of amorphous Fe-Ni-P alloys increases with Fe content. Emergence and recrystallization of stable phases defer as the P content of the coating increases. The minimum H-c, B-r and P-h occur at 9.4 P (wt pet) content. Maximum H-c, B-r and P-h occur at the weight ratio of Fe to Ni equaling to 1/9.