A DEVELOPMENT STUDY OF CAST COPPER ALLOYWITH HIGH STRENGTH AND HEAT-RESISTANCE 被引量:1

A DEVELOPMENT STUDY OF CAST COPPER ALLOY WITH HIGH STRENGTH AND HEAT-RESISTANCE
下载PDF
导出
摘要 By means of Precipitation hardening, a cast copper alloy with high strength and heatresistance named Cu-6Ti-Cr-Al has been developed. This alloy has good castability. After water quenching at 860℃ for 1 h and aging at 450℃ for 4 h, the tensile strength, σ_b, is greater than 890MPa and the compressive strength, σ_(bc), reaches 1300MPa, while the ratio of compression, ε_c, is maintained at 20%. When the environmental temperature is raised to 450℃, the mechanical properties do not show any appreciable loss. These copper alloy castings have been used on the roll sleeves of rubber formers and the journal bearings of sheet mills. The results have shown that the service life of these parts is much longer than that of aluminium bronze and 904alloy castings. In the present work, the microstructure, mechanical properties and strengthening mechanism were investigated. By means of Precipitation hardening, a cast copper alloy with high strength and heatresistance named Cu-6Ti-Cr-Al has been developed. This alloy has good castability. After water quenching at 860℃ for 1 h and aging at 450℃ for 4 h, the tensile strength, σ_b, is greater than 890MPa and the compressive strength, σ_(bc), reaches 1300MPa, while the ratio of compression, ε_c, is maintained at 20%. When the environmental temperature is raised to 450℃, the mechanical properties do not show any appreciable loss. These copper alloy castings have been used on the roll sleeves of rubber formers and the journal bearings of sheet mills. The results have shown that the service life of these parts is much longer than that of aluminium bronze and 904alloy castings. In the present work, the microstructure, mechanical properties and strengthening mechanism were investigated.
出处 《Acta Metallurgica Sinica(English Letters)》 SCIE EI CAS CSCD 1996年第3期217-222,共6页 金属学报(英文版)
关键词 cast copper alloy mechanical properties MICROSTRUCTURE precipitation hardening cast copper alloy, mechanical properties, microstructure, precipitation hardening
  • 相关文献

同被引文献18

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部