Phase equilibrium in the ternary CuO-PbO-Ag system has been investigated using differential thermal analysis(DTA),thermogravimetry(TG),scanning electron microscopy(SEM) and X-ray diffraction(XRD) techniques.In the ternary CuO-PbO-Ag system,there is a eutectic reaction CuO+PbO+Ag=L at 750℃ and a composition of 12.04 mol.% Ag,16.35 mol.% CuO and 71.61 mol.% PbO.Two miscibility gaps near the two binary tie lines PbO-Ag and CuO-Ag were detected. No binary or ternary compound was detected in the ternary system.SEM and energy dispersive spectroscopy(EDS) confirm the presence of two liquid phases and the eutectic point.
Phase equilibrium in the ternary CuO-PbO-Ag system has been investigated using differential thermal analysis(DTA),thermogravimetry(TG),scanning electron microscopy(SEM) and X-ray diffraction(XRD) techniques.In the ternary CuO-PbO-Ag system,there is a eutectic reaction CuO+PbO+Ag=L at 750℃ and a composition of 12.04 mol.% Ag,16.35 mol.% CuO and 71.61 mol.% PbO.Two miscibility gaps near the two binary tie lines PbO-Ag and CuO-Ag were detected. No binary or ternary compound was detected in the ternary system.SEM and energy dispersive spectroscopy(EDS) confirm the presence of two liquid phases and the eutectic point.