摘要
MoSi_2 and 30 vol.% SiC_p/MoSi_2 composite have been fabricated by hot pressing (HP).A simulated thermal cycle experiment has been carried out at 1100℃ for 32 h to investigate the stability of the composite system.Comparative,mechanical tests,including measurement of flexural strength and fracture toughness at room temperature,have been conducted between materials before and after thermal cycle.It is shown that both the strength and fracture toughness are enhanced by the addition of SiC particles. After thermal cycle,the strength of both materials increases and the toughness decreases by about 20%.The result that the composite system is not corroded intensely by thermal cycle shows that SiC particles are feasible reinforcement for MoSi2.
MoSi_2 and 30 vol.% SiC_p/MoSi_2 composite have been fabricated by hot pressing (HP).A simulated thermal cycle experiment has been carried out at 1100℃ for 32 h to investigate the stability of the composite system.Comparative,mechanical tests,including measurement of flexural strength and fracture toughness at room temperature,have been conducted between materials before and after thermal cycle.It is shown that both the strength and fracture toughness are enhanced by the addition of SiC particles. After thermal cycle,the strength of both materials increases and the toughness decreases by about 20%.The result that the composite system is not corroded intensely by thermal cycle shows that SiC particles are feasible reinforcement for MoSi2.