Blends of polyphenylene sulfide (PPS) containing trace amounts of branching and/or cross-linking in chain and Polyamide-66 (PA-66) have been prepared by melt blending. The rheological behavior of PPS/PA-66 blends has been studied by means of capillary rheometer, and compared with PPS. The effects of shear rate, shear stress and temperature on the how of PPS/PA-66 blends and PPS are discussed. The non-Newtonian indexes and the activation energies of viscous how are obtained. The results show that the apparent viscosity of PPS/PA-66 blends is not sensitive to shear rate and stress, but decreases with the elevation of temperature. On the contrary, the apparent viscosity of the PPS decreases obviously with the increasing of shear rate and shear stress, but it is increased by the elevation of temperature.
Blends of polyphenylene sulfide (PPS) containing trace amounts of branching and/or cross-linking in chain and Polyamide-66 (PA-66) have been prepared by melt blending. The rheological behavior of PPS/PA-66 blends has been studied by means of capillary rheometer, and compared with PPS. The effects of shear rate, shear stress and temperature on the how of PPS/PA-66 blends and PPS are discussed. The non-Newtonian indexes and the activation energies of viscous how are obtained. The results show that the apparent viscosity of PPS/PA-66 blends is not sensitive to shear rate and stress, but decreases with the elevation of temperature. On the contrary, the apparent viscosity of the PPS decreases obviously with the increasing of shear rate and shear stress, but it is increased by the elevation of temperature.
基金
This work was supported by the National High Technology Program Fund(863)of China.