摘要
The effect of rare earth(RE) on low frequency high temperature fatigue strength of hot rolled steel 60CrMnMo was investigated. The results show that by adding a certain amount of RE in steel 60CrMnMo, its serviceable life during low frequency fatigue test at high temperature can be improved.The number of cycles for fracture was increased by 18.5%～28.8%. The number of large inclusion particleswas reduced and the composition of inclusions and their shape were changed as well. The strip distances on fatigue fracture surface were decreased. It is concluded that the optimum amount of RE addtion is about 0.05 wt%～0. 10 wt%.
The effect of rare earth(RE) on low frequency high temperature fatigue strength of hot rolled steel 60CrMnMo was investigated. The results show that by adding a certain amount of RE in steel 60CrMnMo, its serviceable life during low frequency fatigue test at high temperature can be improved.The number of cycles for fracture was increased by 18.5%～28.8%. The number of large inclusion particleswas reduced and the composition of inclusions and their shape were changed as well. The strip distances on fatigue fracture surface were decreased. It is concluded that the optimum amount of RE addtion is about 0.05 wt%～0. 10 wt%.