摘要
The process parameters for bath autogenous smelting of copper were selected based on dynamic analysis of the experimental data and calculation of the mathematical model. Selecting the slag composition of SiO<sub>2</sub>/Fe=0.80 and CaO％=16. desulphur ratio less than 80 wt.-％ in system. and the copper content of matte less than 60 wt.-％, it is able to limit Fe<sub>3</sub>O<sub>4</sub> formation and obtain a high desulphurization. The critical oxygen content of the blast increased with decrease of the sulphur content of the concentrate and increase of copper contents of the matte. If the copper contents of the concentrate are respectively of 30 and 35 wt.-％, the critical oxygen contents of the blast will be 48 and 69 wt.-％ respectively. The smelling rate increases linearly with the blast intensity. When the sulphur content of the concentrate is 30 wt.-％, the oxygen content of the blast 70 vol.-％ and the copper content of the matte 60 wt.-％, a blast intensityy of 700 Nm<sup>3</sup>/m<sup>2</sup>·h results in a smeling rate of 48.81 t/m<sup>2</sup>·d.
The process parameters for bath autogenous smelting of copper were selected based on dynamic analysis of the experimental data and calculation of the mathematical model. Selecting the slag composition of SiO_2/Fe=0.80 and CaO％=16. desulphur ratio less than 80 wt.-％ in system. and the copper content of matte less than 60 wt.-％, it is able to limit Fe_3O_4 formation and obtain a high desulphurization. The critical oxygen content of the blast increased with decrease of the sulphur content of the concentrate and increase of copper contents of the matte. If the copper contents of the concentrate are respectively of 30 and 35 wt.-％, the critical oxygen contents of the blast will be 48 and 69 wt.-％ respectively. The smelling rate increases linearly with the blast intensity. When the sulphur content of the concentrate is 30 wt.-％, the oxygen content of the blast 70 vol.-％ and the copper content of the matte 60 wt.-％, a blast intensityy of 700 Nm^3/m^2·h results in a smeling rate of 48.81 t/m^2·d.
出处
《中国有色金属学会会刊：英文版》
CSCD
1993年第1期27-31,共5页
Transactions of Nonferrous Metals Society of China