The growing process of thermal fatigue cracking,in steel 3Cr2WSV was observed under deskSEM fitted with sell-made minisized device for thermal faligue test.Before the growing ofthermal fatigue crack,the main crack tip reveals to blunt firstly,and some holes anduncontinuous microcraeks occur in front of it.The growth is developed by bridging of maincrack together with holes and microcracks.
The growing process of thermal fatigue cracking,in steel 3Cr2WSV was observed under desk SEM fitted with sell-made minisized device for thermal faligue test.Before the growing of thermal fatigue crack,the main crack tip reveals to blunt firstly,and some holes and uncontinuous microcraeks occur in front of it.The growth is developed by bridging of main crack together with holes and microcracks.