Poly(lithium propionate methyl siloxane )as a single-ion carrier source was synthesized. The crosslinked film showed lower lithium ionic conductivity at room temperature (about 10^(-10) S/cm). However,the lithium ionic conductivity was obviously increased by blending with high polar polymers such as polyethylene oxide, poly (methylsiloxane - co- ethylene oxide) and poly (methylsiloxane- g- ethylene oxide). In the blend system a high conductivity of 10^(-7)-10^(-5) Scm^(-1) at room temperature was obtained and the single-ion conductivity was deeply influenced by the content of the poly (lithium propionate methyl siioxane). The dc ionic conductivity of the flexible crosslinked films is more stable over time.
Poly(lithium propionate methyl siloxane )as a single-ion carrier source was synthesized. The crosslinked film showed lower lithium ionic conductivity at room temperature (about 10^(-10) S/cm). However,the lithium ionic conductivity was obviously increased by blending with high polar polymers such as polyethylene oxide, poly (methylsiloxane - co- ethylene oxide) and poly (methylsiloxane- g- ethylene oxide). In the blend system a high conductivity of 10^(-7)-10^(-5) Scm^(-1) at room temperature was obtained and the single-ion conductivity was deeply influenced by the content of the poly (lithium propionate methyl siioxane). The dc ionic conductivity of the flexible crosslinked films is more stable over time.
基金
This work was supported by the National Natural Science Foundation of China