In this letter the study of Li-doped zinc oxide by electron paramagnetic resonance method is described.A signal observed at g_=2.013,g_=1.955 on the degassed sample at 923K was designated to F_s^+ centers(surface oxygen ion vacancies with a single trapped electron).When the sample was quenched from 1003K into liquid oxygen at 77K under 24 KPa O_2,[Li^+O^-] ion pairs valued at g_=2.026 and g=2.003 with superhyperfine constant a=2.0G,which resulted from ~7Li nucleus,formed at Li^+-substitutional site in ZnO lattice.A probable mechanism of [Li^+O^-]ion pair formation was proposed.
In this letter the study of Li-doped zinc oxide by electron paramagnetic resonance method is described.A signal observed at g_=2.013,g_=1.955 on the degassed sample at 923K was designated to F_s^+ centers(surface oxygen ion vacancies with a single trapped electron).When the sample was quenched from 1003K into liquid oxygen at 77K under 24 KPa O_2,[Li^+O^-] ion pairs valued at g_=2.026 and g=2.003 with superhyperfine constant a=2.0G,which resulted from ~7Li nucleus,formed at Li^+-substitutional site in ZnO lattice.A probable mechanism of [Li^+O^-]ion pair formation was proposed.
基金
Supported by Chinese National Scientific Foundation