In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ for Polyamide-1010 samples with various annealing treatment.Through extrapolating method,the Tg obtained was approximately 58℃.Based on the one-dimensional electron density correlation function of partially crystalline polymers,some structural parameters of Polyamide-1010 were determined by SAXS.
In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ for Polyamide-1010 samples with various annealing treatment.Through extrapolating method,the Tg obtained was approximately 58℃.Based on the one-dimensional electron density correlation function of partially crystalline polymers,some structural parameters of Polyamide-1010 were determined by SAXS.