摘要
Microstructure of the deepest zone of high speed steel W6Mo5Cr4V2(M2)melt after laser fu-sion was found to be so fine as the ehill zone of a solidified ingot.When narrower chill zoneformed,the long columnar dendrites grow into the melt and then the fine equiaxed cellularstructure appears in upper melt region nearly surface.The substructure of cellular grains anddendrites was observed to consist of martensite and retained austenile,while the carbides asM_6C_■ Cr_7C_3 and MC distributed at their boundaries.It is believed that the highermicrohardness up to HV_(0.1)=865-960 of the laser fused structure of the alloy is due to the oc-currence of martensite.
Microstructure of the deepest zone of high speed steel W6Mo5Cr4V2(M2)melt after laser fu-sion was found to be so fine as the ehill zone of a solidified ingot.When narrower chill zoneformed,the long columnar dendrites grow into the melt and then the fine equiaxed cellularstructure appears in upper melt region nearly surface.The substructure of cellular grains anddendrites was observed to consist of martensite and retained austenile,while the carbides asM_6C_■ Cr_7C_3 and MC distributed at their boundaries.It is believed that the highermicrohardness up to HV_(0.1)=865-960 of the laser fused structure of the alloy is due to the oc-currence of martensite.
作者
LIU Ning CUI Kun Huazhong University of Science and Technology,Wuhan.China DENG Zonggang Hefei University of Technology,Hefei,China CHENG Benpei KONG Jie Institute of Solid State Physics,Academia Sinica,Hefei,China Doctorate student,Department of Mechanical Engineering No.2,Huazhong University of Science and Technology,Wuhan 430074,China