BN films,synthesized by ion beam assisted deposition,were analysed by RBS,AES, IR spectra and TEM.Formatiom of c-BN phase was shown not only by IR spectra at absorption peak of 1100 cm^(-1),but also by electron diffraction pattern.The results of AES demonstrate an effect of N^+ implantation near the film surface.The deposited films consist of three layers,i.e.,ion implantation layer,film layer and mixed intermediatelayer, according to the difference of concentration.The micro-Knoop hardness of the film is 25—35 GPa.
BN films,synthesized by ion beam assisted deposition,were analysed by RBS,AES, IR spectra and TEM.Formatiom of c-BN phase was shown not only by IR spectra at absorption peak of 1100 cm^(-1),but also by electron diffraction pattern.The results of AES demonstrate an effect of N^+ implantation near the film surface.The deposited films consist of three layers,i.e.,ion implantation layer,film layer and mixed intermediatelayer, according to the difference of concentration.The micro-Knoop hardness of the film is 25—35 GPa.