The addition of Pb in the superconductors of BiSrCaCuO system is very helpful for growth of the high-Tc phase (Tc 110K). We prepared a series of samples with nominal composition of Bi2-xPbxSr2Ca2Cu3Oy (0.1&lex&le2). The zero resistance transition temperature Tc of 106K and the critical transport current density Jc of 1 × 103A/cm2 at 77K have been obtained for the samples of Bi2-xPbxSr2Ca2Cu3Oy (x=0.2 and 0.3). The X-ray diffraction analysis and measurement of AC magnetic susceptibility confirmed that the material is comprised of single high-Tc phase. We also report the magnetic properties of this material as well as the results of TEM observation.
The addition of Pb in the superconductors of BiSrCaCuO system is very helpful for growth of the high-Tc phase (Tc 110K). We prepared a series of samples with nominal composition of Bi2-xPbxSr2Ca2Cu3Oy (0.1&lex&le2). The zero resistance transition temperature Tc of 106K and the critical transport current density Jc of 1 × 103A/cm2 at 77K have been obtained for the samples of Bi2-xPbxSr2Ca2Cu3Oy (x=0.2 and 0.3). The X-ray diffraction analysis and measurement of AC magnetic susceptibility confirmed that the material is comprised of single high-Tc phase. We also report the magnetic properties of this material as well as the results of TEM observation.
基金
This work was supported by The National Center for Research and Development on Superconductivity.