Upon heating, Mn atoms implanted into Na - beta- alumina diffuse inwards andoutwards with an activation energy of 0.96 eV, and substitute for Al3+ in the spinel layers of the crystal. For specimens annealed at 900 C, the optical absorption shows remarkable change in 190nm-400nm wavelength region. They fluoresce brightly green and a well- defined peak (at 525 nm) has been found in the radiative spectra.
Upon heating, Mn atoms implanted into Na - beta- alumina diffuse inwards andoutwards with an activation energy of 0.96 eV, and substitute for Al3+ in the spinel layers of the crystal. For specimens annealed at 900 C, the optical absorption shows remarkable change in 190nm-400nm wavelength region. They fluoresce brightly green and a well- defined peak (at 525 nm) has been found in the radiative spectra.