The oxygen relief/absorption,superconduc— tivity and structure of(Bi_(1-x)Pb_x)_2Sr_2Ca_2— Cu_3O_y compounds have been studied by TGA, electrical resistance measurement and X-ray diffraction.The amount of oxygen which can be re- leased and superconductivity of the compounds are correlative to Pb content.The release of oxygen in- creases when x less than 0.2 and decreases when x exceeds 0.2 with increasing x.The appropriate con- tent of Pb for superconductivity is in the range of 0.1<x<0.3,which corresponds to the relative large amount of oxygen that can be released.It is found according to electric resistance measurement that quenching is favourable to form the‘85K’phase and slow cooling the‘110K’phase.The experimen- tal results suggest that a relation exists between the superconductivity and the oxygen content in Bi sys- tem containing Pb.As the T_c of‘85K’phase de- creases and that of‘110K’phase increases with in- creasing oxygen content,it is possible that the effect of oxygen content in‘85K’phase and‘110K’ phase on the superconductivity is different.
The oxygen relief/absorption,superconduc— tivity and structure of(Bi_(1-x)Pb_x)_2Sr_2Ca_2— Cu_3O_y compounds have been studied by TGA, electrical resistance measurement and X-ray diffraction.The amount of oxygen which can be re- leased and superconductivity of the compounds are correlative to Pb content.The release of oxygen in- creases when x less than 0.2 and decreases when x exceeds 0.2 with increasing x.The appropriate con- tent of Pb for superconductivity is in the range of 0.1<x<0.3,which corresponds to the relative large amount of oxygen that can be released.It is found according to electric resistance measurement that quenching is favourable to form the‘85K’phase and slow cooling the‘110K’phase.The experimen- tal results suggest that a relation exists between the superconductivity and the oxygen content in Bi sys- tem containing Pb.As the T_c of‘85K’phase de- creases and that of‘110K’phase increases with in- creasing oxygen content,it is possible that the effect of oxygen content in‘85K’phase and‘110K’ phase on the superconductivity is different.