F mineral admixture (FMA) is made of the fin- ely divided powder of natural zeolite with a bit of other agent. When FMA is used to displace about 10% (by weight) of the ordinary portland cement (OPC) (strength grade 575#) in concrete and mixed with a suitable amount of super plasticizer (w/c =0.31-0.35), then a high-strength concrete with compressive strength about 80 MPa and slump about 180 MM can be obtained. The strength of this concrete is about 10-15% higher than that of the corresponding concrete mixing with pure OPC, and its bleeding decreases greatly. It makes no segre- gation and separation, and thus it satisfies the requirement of pumping concrete in construction.
F mineral admixture (FMA) is made of the fin- ely divided powder of natural zeolite with a bit of other agent. When FMA is used to displace about 10% (by weight) of the ordinary portland cement (OPC) (strength grade 575#) in concrete and mixed with a suitable amount of super plasticizer (w/c =0.31-0.35), then a high-strength concrete with compressive strength about 80 MPa and slump about 180 MM can be obtained. The strength of this concrete is about 10-15% higher than that of the corresponding concrete mixing with pure OPC, and its bleeding decreases greatly. It makes no segre- gation and separation, and thus it satisfies the requirement of pumping concrete in construction.