Suspension of micrometer-sized 1,4-bis（4-methylstyryl）benzene（p-MSB） was converted into colloidal nanocrystal solution by irradiation with an femtosecond laser（800 nm, 1 kHz）. The prepared nanocrystals were rectangular with ca. 100 nm in size. The same crystal structure as that of bulk crystals was confirmed by X-ray diffraction measurement. UV-Vis spectra and emission spectra of the nanoparticle dispersions in dichloromethane（poor solvent） were examined. The nanocrystal exhibits large quantum yield（89%）. The nonlinear optical properties of the nanocrystals were further studied by Z-scan technique with femtosecond laser duration of 120 fs at a wavelength of 800 nm. The results show that the nanocrystals exhibit strong nonlinear absorption.
Suspension of micrometer-sized 1,4-bis（4-methylstyryl）benzene（p-MSB） was converted into colloidal nanocrystal solution by irradiation with an femtosecond laser（800 nm, 1 kHz）. The prepared nanocrystals were rectangular with ca. 100 nm in size. The same crystal structure as that of bulk crystals was confirmed by X-ray diffraction measurement. UV-Vis spectra and emission spectra of the nanoparticle dispersions in dichloromethane（poor solvent） were examined. The nanocrystal exhibits large quantum yield（89%）. The nonlinear optical properties of the nanocrystals were further studied by Z-scan technique with femtosecond laser duration of 120 fs at a wavelength of 800 nm. The results show that the nanocrystals exhibit strong nonlinear absorption.
基金
Supported by the National High-Tech Research and Development Program of China(No.2009AA03Z401)
the National Natural Science Foundation of China(Nos.61077002,60807030)