摘要
The corrosion to asphalt mixture under different kinds of corrosion solution, such as pH=2 solution, pH=12 solution, pH = 12 solution and 10% Na2SO4 solution, was studied. The performance attenuation of asphalt mixture was analyzed under the normal environment and the freeze-thaw environment, and the analysis was given on the sensitivity of the test results to the evaluation index. The experimental results show that the performance of asphalt mixture is attenuated faster under the acidic solution, alkaline solution and sulfate solution. Corrosion factor Kc, freeze-thaw corrosion factor Kf, and freeze-thaw effect factor Kfc are proposed to evaluate asphalt mixture resistance to corrosion in different kinds of corrosion solution. The values of Kc and Kfc decrease with the increasing of corrosion time. The change rule of Kf show that the rate of corrosion is decreased by the action of freeze-thaw in acidic solution and in alkaline solution, but is increased by the action of freeze-thaw in sulfate solution. The microscopic analysis indicates that acid solution reacts with aggregate of asphalt mixture, alkaline solution reacts with asphalt cement of asphalt mixture, the surface tension of sulfate solution and crystallization of sulfate are the main reasons which weak the performance of asphalt mixture.
The corrosion to asphalt mixture under different kinds of corrosion solution, such as pH=2 solution, pH=12 solution, pH = 12 solution and 10% Na2SO4 solution, was studied. The performance attenuation of asphalt mixture was analyzed under the normal environment and the freeze-thaw environment, and the analysis was given on the sensitivity of the test results to the evaluation index. The experimental results show that the performance of asphalt mixture is attenuated faster under the acidic solution, alkaline solution and sulfate solution. Corrosion factor Kc, freeze-thaw corrosion factor Kf, and freeze-thaw effect factor Kfc are proposed to evaluate asphalt mixture resistance to corrosion in different kinds of corrosion solution. The values of Kc and Kfc decrease with the increasing of corrosion time. The change rule of Kf show that the rate of corrosion is decreased by the action of freeze-thaw in acidic solution and in alkaline solution, but is increased by the action of freeze-thaw in sulfate solution. The microscopic analysis indicates that acid solution reacts with aggregate of asphalt mixture, alkaline solution reacts with asphalt cement of asphalt mixture, the surface tension of sulfate solution and crystallization of sulfate are the main reasons which weak the performance of asphalt mixture.
基金
Funded by the National Natural Science Foundation of China(No.50978031)
the Special Fund for Basic Scientific Research of Central Colleges, Chang'an University (No.CHD2010ZY014)