Dissolution of Al_2TiO_5 inclusions in CaO-SiO_2-Al_2O_3 slags at 1823 K 被引量:3

Dissolution of Al_2TiO_5 inclusions in CaO-SiO_2-Al_2O_3 slags at 1823 K
下载PDF
导出
摘要 Al-Ti-O inclusions always clog submerged nozzles in Ti-bearing Al-killed steel.A typical synthesized Al2TiO5 inclusion was immersed in a CaO-SiO2-Al2O3 molten slag for different durations at 1823 K.The Al2TiO5 dissolution paths and mechanism were revealed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).Decreased amounts of Ti and Al and increased amounts of Si and Ca at the dissolution boundary prove that inclusion dissolution and slag penetration simultaneously occur.SiO2 diffuses or penetrates the inclusion more quickly than CaO,as indicated by the w(CaO)/w(SiO2) value in the reaction region.A liquid product (containing 0.7-1.2 w(CaO)/w(SiO2),15wt%-20wt% Al2O3,and 5wt%-15wt% TiO2) forms on the inclusion surface when Al2TiO5 is dissolved in the slag.Al2TiO5 initially dissolves faster than the diffusion rate of the liquid product toward the bulk slag.With increasing reaction time,the boundary reaches its largest distance,the Al2TiO5 dissolution rate equals the liquid product diffusion rate,and the dissolution process remains stable until the inclusion is completely dissolved. Al-Ti-O inclusions always clog submerged nozzles in Ti-bearing Al-killed steel.A typical synthesized Al2TiO5 inclusion was immersed in a CaO-SiO2-Al2O3 molten slag for different durations at 1823 K.The Al2TiO5 dissolution paths and mechanism were revealed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).Decreased amounts of Ti and Al and increased amounts of Si and Ca at the dissolution boundary prove that inclusion dissolution and slag penetration simultaneously occur.SiO2 diffuses or penetrates the inclusion more quickly than CaO,as indicated by the w(CaO)/w(SiO2) value in the reaction region.A liquid product (containing 0.7-1.2 w(CaO)/w(SiO2),15wt%-20wt% Al2O3,and 5wt%-15wt% TiO2) forms on the inclusion surface when Al2TiO5 is dissolved in the slag.Al2TiO5 initially dissolves faster than the diffusion rate of the liquid product toward the bulk slag.With increasing reaction time,the boundary reaches its largest distance,the Al2TiO5 dissolution rate equals the liquid product diffusion rate,and the dissolution process remains stable until the inclusion is completely dissolved.
出处 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2011年第6期646-651,共6页 矿物冶金与材料学报(英文版)
基金 supported by the National Natural Science Foundation of China (No.50904017)
关键词 steelmaking aluminium titante molten slag inclusions dissolution steelmaking aluminium titante molten slag inclusions dissolution
  • 相关文献

参考文献15

  • 1K. Yamamoto, T. Hasegawa, and J. Takamura, Effect of boron on intra-granular ferrite formation in Ti-oxide beating steels, ISIJ Int., 36(1996), No. 1, p.80.
  • 2L.M. Peng, Z. Li, and H. Li, Effects of microalloying and ceramic particulates on mechanical properties of TiAl-based alloys, J. Mater. Sci., 41(2006), No.22, p.7524.
  • 3M. Vedani and A. Marmucci, Effect of titanium addition on precipitate and microstructural control in C-Mn microalloyed steel, ISIJlnt., 42(2002), No. 12, p. 1520.
  • 4Y. Kawashima, Y. Nagata, and K. Shinme, Influence of Ti concentration on nozzle clogging on Al-Ti deoxidation: behavior of inclusion on A1-Ti deoxidation-2, CAMP-ISIJ, 4(1991), No.4, p.1237.
  • 5S. Basu, S.K. Choudhary, and N.U. Girase, Nozzle clogging behaviour of Ti-bearing Al-killed ultra low carbon steel, ISIJ Int., 44(2004), No.10, p.1653.
  • 6I.H. Jung, S.A. Decterov, and A.D. Pelton, A thermodynamic model for deoxidation equilibrium in steel, Metall. Mater. Trans. B, 35(2004), No.3, p.493.
  • 7M.K. Sun, I.H. Jung, and H.G. Lee, Morphology and chemistry of oxide inclusions after AI and Ti complex deoxidation, Met. Mater. lnt., 14(2008), No.6, p.791.
  • 8W.C. Doo, D.Y. Kim, S.C. Kang, et al., The morphology of A1-Ti-O complex oxide inclusions formed in an ultra low-carbon steel melt during the RH process, Met. Mater. lnt., 13(2007), No.3, p.249.
  • 9F. Ruby-Meyer, J. Lehmarm, and H. Gaye, Thermodynamic analysis of inclusion in Ti-deoxidized steel, Scand.J.. Metall., 29(2000), No.5, p.206.
  • 10Y. Oishi, A.R. Cooper Jr., and W.D. Kingery, Dissolution in ceramic systems: III. Boundary layer concentration gradients, J. Am. Ceram. Soc., 48(1965), No.2, p.88.

同被引文献73

引证文献3

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部