摘要
通过对某军工产品用50SiMnVB钢在加热过程中,横向断裂疵病产生的原因机理进行了分析与验证,准确地找到了该问题产生的原因,并在后续生产中增加无损检测技术,可有效地剔除该类缺陷,保证产品质量。
The mechanism of transverse rupture defects of a military product with 50SiMnVB steel in heating process was analyzed and verified, and the cause was found. Nondestructive testing technology was added in subsequent production, which could be effectively used to eliminate the defects, and guarantee the product quality.
出处
《精密成形工程》
2012年第1期78-81,共4页
Journal of Netshape Forming Engineering
关键词
横向断裂
分析与验证
质量
无损检测
transverse fracture
analysis and verification
quality
nondestructive testing