A water-cooled serpentine channel pouring process was invented to produce semi-solid A356 aluminum alloy slurry for rheocast ing, and the effects of pouring temperature and circulating cooling water flux on the microstmcture of the slurry were investigated. The results show that at the pouring temperature of 640-680~C and the circulating cooling water flux of 0.9 m3/h, the semi-solid A356 aluminum alloy slurry with spherical primary a（A1） grains can be obtained, whose shape factors are between 0.78 and 0.86 and the grain diameter can reach 48-68 ~am. When the pouring temperatures are at 660-680~C, only a very thin solidified shell remains inside the serpentine channel and can be removed easily. When the serpentine channel is cooled with circulating water, the microstructure of the semi-solid slurry can be improved, and the serpentine channel is quickly cooled to room temperature after the completion of one pouring. In terms of the productivity of the special equipment, the water-cooled serpentine channel is economical and efficient.
A water-cooled serpentine channel pouring process was invented to produce semi-solid A356 aluminum alloy slurry for rheocast ing, and the effects of pouring temperature and circulating cooling water flux on the microstmcture of the slurry were investigated. The results show that at the pouring temperature of 640-680~C and the circulating cooling water flux of 0.9 m3/h, the semi-solid A356 aluminum alloy slurry with spherical primary a（A1） grains can be obtained, whose shape factors are between 0.78 and 0.86 and the grain diameter can reach 48-68 ~am. When the pouring temperatures are at 660-680~C, only a very thin solidified shell remains inside the serpentine channel and can be removed easily. When the serpentine channel is cooled with circulating water, the microstructure of the semi-solid slurry can be improved, and the serpentine channel is quickly cooled to room temperature after the completion of one pouring. In terms of the productivity of the special equipment, the water-cooled serpentine channel is economical and efficient.
基金
financially supported by the National Natural Science Foundation of China (No.50774007)
the National High-Tech Research and Development Program of China (No.2006AA03Z115)
the National Basic Research Priorities Program of China(No.2011CB606302-1.)